DESCRIPTION
Aqua-Loc Ceramic Topcoat is a strong, tough coating, formulated with hollow-core ceramic microspheres, strands and irregular particulate in a complex 100% acrylic suspension with superior adhesion and abrasion resistance. Provides significant resistance to cracking, chalking. peeling and weathering. Exhibits exceptional adhesive and thermal properties. Aqua-Loc Ceramic Topcoat is intended to be a topcoat providing an extension to the existing roofing system and is not a stand-alone roofing material.
USAGE
Aqua-Loc Ceramic Topcoat is ideal for use on Commercial, Industrial, Government, and Residential buildings.
Roof systems include:
• Built-Up, Modified Bitumen, and Cold-Process Systems
• Asphalt and Fiber-Cement Shingles
• Synthetic Rubber Single-Ply Systems
• Concrete Roofs, Concrete and Fired Clay Tiles
• Galvanized Steel, Aluminum, and Enameled Steel
• Wood Shake and Shingles
Pastel/White base is recommended for peak thermal benefits.
ADVANTAGES
|
Cost Savings |
Fire Resistant |
Environmentally Friendly |
-Increases Efficiency
-Slows movement of heat and provides heat management
-Greater comfort, reduced energy consumption
|
-Self Extinguishing
-Does not support flame spread |
-Modified acrylic water-based products
-Green product that meets increasingly strict Environmental guidelines
-Valuable component of emerging sustainable design programs
|
|
UV RESISTANT |
WEATHERPROOFING |
THERMAL BARRIER |
|
-Excellent UV Inhibitor |
-Creates weatherproof membrane reducing damage and deterioration. |
-Can withstand thermal cycling
-High solar reflectance and thermal emmitance |
|
COLOUR CHOICES |
|
|
-Resists fading
-White, pastels and accent colours
-Easy to apply |
|
|
THIS PRODUCT IS NOT SUBJECT TO THE CONTROLLED PRODUCTS REGULATIONS
|
CHARACTERISTICS |
TEST METHOD |
OBSERVATION |
|
Weight per US Gallon (3.78L) |
FTMS 141 – Method 4184 |
11 LB (4.99Kg) |
|
Non-Volatile Solids |
FTMS 141 – Method 4041 |
By weight: 69.1%
By volume: 60.9% |
|
Viscosity |
FTMS 141 – Method 4281 |
Stormer Viscosity: 100 revolutions in 8 seconds at 500 grams |
|
Toxicity |
FTMS 141 – Method 511 |
Material is non-toxic & requires no special ventilation during
application.
Contains no materials considered to be health hazards |
|
Flammability |
ASTM 1360 – DOT – MVSS 302 |
In container: Non-flammable. On concrete: Self-extinguishing-does not support flame spread.
|
|
Package Stability |
|
One year + after opening: no settling or other undesirable effects Materials completely dispersed after stirring. |
|
Abrasion Resistance |
FTMS 141 – Method 6192 Tabor C17 Wheel - 100 grams - 1000 cycles
|
Weight loss in grams: InsulCoat Roof with aggregate 41 g InsulCoat Roof without aggregate 14 g Epoxy floor coating without aggregate 9 g (Typical) |
|
Hardness |
ASTM D2370 |
6H – This is the hardest value measured by this test and compares to a typical 2H hardness of hardwood floor finishes. |
|
Impact Resistance |
ASTM D2794 |
28 inch-pounds of impact with no break in the film surface. Typically, 20 inch-pounds of impact is considered to be a high performance test result. |
|
Water Resistance (wind-driven rain) |
TTC-555 Time for water to penetrate: Water driven against test surface at a dynamic pressure equivalent to 98 mph |
Time for water to penetrate: One Coat 6.3 mils 30 minutes Two Coats 10.0 mils 11 hours Two Coats 12.0 mils none at 24 hours |
|
High Humidity Resistance |
FTMS 141 – Method 6201 100% condensing humidity at 107° F – 41.67° C |
336 hours with no evidence of film deterioration, blistering or peeling from substrate (250 hours required to pass Federal Specifications). |
|
Salt Spray |
FTMS 141 – Method 811.1 100% condensing 5% salt fog at 95° F – 35° C |
336 hours with no evidence of film deterioration, blistering or peeling from substrate. (250 hours required to pass Federal Specifications). |
|
Fungus Resistance |
FTMS 141 – Method 6271 |
No fungus growth when material tested in an environment of three organisms |
Ceramic base TOP COAT paint
Metal Roofs |
TOP COAT ceramic base paint
BEFORE |
TOP COAT ceramic base paint
DURING |
TOP COAT ceramic base paint
AFTER |
TOP COAT ceramic base paint
AFTER |
|